PROPERTY | UNIT | VALUE / RANGE |
Melting Point | °C | 255 |
Density | g mL-1 | 1.35 - 1.40 |
Coefficient of Thermal Expansion x 10-5 | cm / (cm °C) | 6 - 7 |
Heat Deflection Temperature, 0.5 MPa | °C | 80 |
Heat Deflection Temperature, 1.8 MPa | °C | 116 |
Thermal Conductivity | W / mK | 0.15 - 0.24 |
Rockwell Hardness, M/R Scale | n/a | R125 / M93 |
PROPERTY | UNIT | VALUE / RANGE |
Tensile Strength, Yield at 23 C | MPa | 60 - 85.5 |
Tensile Strength, Break at 23 C | MPa | |
Elongation, Yield | % | |
Elongation, Break | % | 20 |
Tensile Modulus at 23 C | MPa | 2800 - 3170 |
Flexural Strength, Yield | MPa | 125 |
Flexural Modulus | MPa | 3380 |
Compressive Strength | MPa | 70 |
Izod Notched | J / m | 1.6 - 22.7 |
Izod Unnotched | J / m |
PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm | > 1013 | |
Dielectric Strength | V/mm x 104 | 5.0 | |
Dielectric Constant @ 1 MHz | n/a | 3.4 - 3.7 | |
Dissipation Factor @ 1 MHz | n/a, x 10-4 | 0.02 |
PROPERTY | UNIT | VALUE / RANGE | |
| °C | ||
Mold Shrinkage | % | ||
Continuous Service Temperature | °C | 100 | |
Water Absorption, 24 hr. Immersion | % | 0.07 - 0.1 |